Al-Braze® EC Aluminum Brazing Flux

Al-Braze® EC Aluminum brazing Flux 1/2 lb. x 1 ea. Jar Features
  • Powdered flux for brazing aluminum alloys
  • This flux can be used dry or mixed with water or alcohol to form a paste
  • Typically used to braze common aluminum base materials such as 1100, 3003 and 6061
  • Works well with aluminum brazing filler metals 4047 (718) and 4145
  • Ideal for torch brazing aluminum
  • Complies with the EU Reach & RoHS directive
  • BRAZING ROD – WESTRON

    Brand: WESTRON® O Phos-Copper Brazing Alloy Solidus – 1310F/710C            .050”x1/8” Liquidus 1475F/802C              (1.27mmx3.2mm) WESTRON Brazing Rod is used in the process of joining metals in which a filler metal is heated and then distributed over base metals joining the work pieces with the help of Brazing Rods. Brazing is the process to form one strong load bearing joint.[/vc_column_text][/vc_column][/vc_row]

    Copper Harris Brazing Rod

    *Made in USA* Product Description Harris Brazing Rod is used in the process of joining metals in which a filler metal is heated and then distributed over base metals joining the work pieces with the help of Brazing Rods. Copper Brazing Rod for the repairing, maintenance, and joining of copper and copper alloys Specifications:
    • 28 Stick Tubes
    • Size: 2 mm
    • Harris 0® - 0% Silver Phos Copper Brazing Rod 0620F1
    • 1/8" X .050 X 20" brazing sticks
    • Chemical Composition: 0% Silver, 7.1% Phosphorus, Balance Copper
    • AWS/A5.8 Class BCuP-2
    • Liquidus Temperature: 1475°F (802°C)
    • Solidus Temperature: 1310°F (710°C)
     

    Harris Blockade®

    Phos-copper-tin-silicon filler metal for low temperature brazing of copper and brass. Diameter
  • 1/8 in (3.2 mm)
  • 2.0 mm (0.08 in)
  • 2.0 x 500 mm (0.08 x 19.7 in)
  • 3/32 in (2.4 mm)
  • Harris® 0

    Harris® 0 is a low-cost alloy that is suitable for most copper-to-copper or brass joints where close tolerance can be maintained. Features
  • Economical choice for copper brazing
  • Copper is self-fluxing
  • Alloy flows quickly at brazing temperature so requires close joint tolerance of less than 0.005 in. (0.13 mm)
  • Primarily used in manual brazing applications
  • Also a suitable for brazing brass
  • Operators should avoid overheating the brass and use Stay-Silv® white brazing flux
  • Not recommended for brazing steel or other ferrous base metals
  • Should not use Harris® 0 if braze is exposed to sulfur or sulfur compounds in service
  • Recommended joint clearance of 0.002 in. - 0.007 in. (0.05 mm - 0.18 mm)
  • Complies with the EU Reach & RoHS directive